Brinell Hardness Testing

แปลว่า(english) Method of determining the hardness of materials; involves impressing a hardened ball of specified diameter into the material surface at a known pressure (10-mm ball, 500-kg load for aluminum alloys). The Brinell hardness number results from calculations involving the load and the spherical area of the ball impression. Direct-reading testing are generally used for routine inspection of forgings, and as a heat treat control function.

Butcher Saw Steel

แปลว่า(english) A hardened, tempered, and polished high carbon spring steel strip material (carbon content is generally higher than that of a material used for wood band saw applications) with a Rockwell value of roughly C47/49.

Linear:

แปลว่า(english) A structure is said to behave linearly when its the deformation response is directly proportional to the loading (i.e. doubling the load doubles the displacement response). For a material, linear means that the stress is directly proportional to the strain.

Brinell Hardness

แปลว่า(english) The hardness of a metal or part, as represented by the number obtained from the ratio between the load applied on the spherical area of the impression made by a steel ball forced into the surface of the material tested.

Bearing Strength

แปลว่า(english) The maximum bearing load at failure divided by the effective bearing area. In a pinned or riveted joint, the iffective area is calculated as the product of the diameter of the hole and the thickness of the bearing member.

Linear Elastic:

แปลว่า(english) A force-displacement relationship which is both linear and elastic. For a structure, this means the deformation is proportional to the loading, and deformations disappear on unloading. For a material, the concept is the same except strain substitutes for deformation, and stress substitutes for load.

Brinell Hardness Number

แปลว่า(english) The value of hardness of a metal on an arbitrary scale representing kg/mm2, determined by measuring the diameter of the impression made by a ball of given diameter applied under a known load. Values are expressed in Brinell Hardness Numbers, BHN

Band Saw Steel (Wood)

แปลว่า(english) A hardened tempered bright polished high carbon cold rolled spring steel strip produced especially for use in the manufacture of band saws for sawing wood, non ferrous metals, and plastics. Usually carries some nickel and with a Rockwell value of approximately C40/45.

Flexibility:

แปลว่า(english) Flexibility is the inverse of stiffness. When a force is applied to a structure, there is a displacement in the direction of the force; flexibility is the ratio of the displacement divided by the force. High flexibility means that a small load produces a large displacement.

Elastic energy:

แปลว่า(english) The energy stored in deformed elastic material (e.g., a watch spring). Elastic energy equals where k is the stiffness, and is the associated deflection. Elastic energy is sometimes called elastic potential energy because it can be recovered when the object returns to its original shape; see potential energy.

Break Test (for tempered steel)

แปลว่า(english) A method of testing hardened and tempered high carbon spring steel strip wherein the specimen is held and bent across the grain in a vice-like calibrated testing machine. Pressure is applied until the metal fractures at which point a reading is taken and compared with a standard chart of brake limitations for various thickness ranges.

Bainite

แปลว่า(english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite.